Bubuka
stainless steels katelah steels alloy tinggi.Éta diwangun ngeunaan 4-30% kromium.Aranjeunna digolongkeun kana martensitic, austenitic, sarta steels ferritic dumasar kana struktur kristal maranéhanana.
Kelas 317 stainless steel mangrupakeun versi dirobah tina 316 stainless steel.Cai mibanda kakuatan tinggi na lalawanan korosi.Lembar data di handap ieu masihan langkung rinci ngeunaan stainless steel kelas 317.
Komposisi Kimia
Baja tahan karat - Kelas 317 (UNS S31700)
Komposisi kimia kelas 317 stainless steel ieu outlined dina tabel di handap ieu.
| unsur | Eusi (%) |
|---|---|
| Beusi, Fe | 61 |
| Kromium, Cr | 19 |
| Nikel, Ni | 13 |
| Molibdenum, Mo | 3.50 |
| Mangan, Mn | 2 |
| Silikon, Si | 1 |
| Karbon, C | 0,080 |
| Fosfor, P | 0.045 |
| Sulfur, S | 0.030 |
Pasipatan fisik
Baja tahan karat - Kelas 317 (UNS S31700)
tabél di handap nembongkeun sipat fisik kelas 317 stainless steel.
| Pasipatan | métrik | Kaisar |
|---|---|---|
| Kapadetan | 8 g/cm3 | 0,289 lb/in³ |
| Titik lebur | 1370°C | 2550°F |
Sipat mékanis
Baja tahan karat - Kelas 317 (UNS S31700)
Sipat mékanis tina annealed kelas 317 stainless steel dipintonkeun dina tabel di handap ieu.
| Pasipatan | métrik | Kaisar |
|---|---|---|
| Kakuatan regangan | 620 MPa | 89900 psi |
| kakuatan ngahasilkeun | 275 MPa | 39900 psi |
| Modulus elastis | 193 GPa | 27993 ksi |
| Babandingan Poisson | 0.27-0.30 | 0.27-0.30 |
| Elongation dina putus (dina 50 mm) | 45% | 45% |
| Teuas, Rockwell B | 85 | 85 |
Sipat termal
Sipat termal tina stainless steel kelas 317 dibere dina tabel di handap ieu.
| Pasipatan | métrik | Kaisar |
|---|---|---|
| Ko-efisien ékspansi termal (@ 0-100°C/32-212°F) | 16 µm/m°C | 8,89 µin/in°F |
| Konduktivitas termal (@ 100°C/212°F) | 16,3 W/mK | 113 BTU in/hr.ft².°F |
Sebutan séjén
Sebutan séjén anu sarua jeung kelas 317 stainless steel kaasup dina tabel di handap ieu.
| ASTM A167 | ASTM A276 | ASTM A478 | ASTM A814 | ASME SA403 |
| ASTM A182 | ASTM A312 | ASTM A511 | QQ S763 | ASME SA409 |
| ASTM A213 | ASTM A314 | ASTM A554 | DIN 1.4449 | MIL-S-862 |
| ASTM A240 | ASTM A403 | ASTM A580 | ASME SA240 | SAE 30317 |
| ASTM A249 | ASTM A409 | ASTM A632 | ASME SA249 | SAE J405 (30317) |
| ASTM A269 | ASTM A473 | ASTM A813 | ASME SA312 |
Fabrikasi sareng Perlakuan Panas
Kamampuh mesin
Pilari alat pikeun nganalisis logam anjeun?
Kelas 317 stainless steel nyaeta tougher ti 304 stainless steel.Disarankeun make breakers chip.Hardenability tina alloy ieu bakal ngurangan lamun feed konstanta sarta speeds low dipaké.
Las
Kelas 317 stainless steel tiasa dilas nganggo metode fusi sareng résistansi.Metoda las oxyacetylene teu pikaresep keur alloy ieu.AWS E / ER317 atanapi 317L pangisi logam tiasa dianggo pikeun kéngingkeun hasil anu saé.
Panas Gawé
Kelas 317 stainless steel tiasa dianggo panas nganggo sadaya prosedur kerja panas anu umum.Ieu dipanaskeun dina 1149-1260 ° C (2100-2300 ° F).Teu kudu dipanaskeun di handap 927°C (1700°F).Annealing pos-karya bisa dipigawé pikeun nahan sipat lalawanan korosi.
Tiis Gawé
Stamping, shearing, gambar, sareng judul tiasa dilakukeun kalayan suksés.Annealing saatos damel dilaksanakeun pikeun ngirangan setrés internal.