Tabél Data
Komposisi kimiawi:
2205 stainless steel coiled tube komposisi kimiawi
| Cr | Ni | Mo | Co | Nb (+Ta) | Ti | V | W | Cu | C | Mn | N | Si | P | S | Fe | Al | |
| Min | 22.00 | 4.50 | 3.00 | 0.14 | 0.20 | ||||||||||||
| Max | 23.00 | 6.50 | 3.50 | 0.03 | 0.20 | 0.70 | 0.03 | 0.02 | Bal |
Sipat mékanis:
2205 stainless steel coiled tube komposisi kimiawi
| 0,2% Buktina Stress | 450 N/mm2 | 65ksi |
| Kakuatan regangan | 655 N/mm2 | 95ksi |
| Élongasi, 5,65√S0 | 25% | |
| Pangurangan wewengkon | 45% | |
| Teu karasa (Brinell) | <270 | |
| Kakuatan Dampak (Suhu Kamar) | 80J (av) | |
| Kakuatan Dampak (-46°C): Longitudinal | <100mm 80J | |
| 100-260mm 45J (35J mnt) | ||
| > 260mm Kanggo inpo wungkul | ||
| Kakuatan Dampak (-46oC): Transversal | 50-260mm 45J (35J mnt) | |
| > 260mm Kanggo inpo wungkul | ||
Catetan:
2205 stainless steel coiled tube komposisi kimiawi
- Uji coba kedah dilaksanakeun saluyu sareng ASTM A370 atanapi EN ISO 6892-1 (tensile), EN ISO 6506-1 (teu karasa)
- Sipat minimum dicutat (diuji dina suhu kamar dina arah longitudinal)
- Uji coba dilakukeun dina unggal lebur bahan per angkatan perlakuan panas
- Teu karasa kedah saluyu sareng NACE MR 1075
- Uji korosi ASTM G48A (dina 25°C) Henteu aya pitting sareng <3.0g/m2leungitna beurat
- Eusi ferit 40-55%
- Mikrostruktur disertipikasi bébas tina karbida wates sisikian, sigma, chi sareng fase laves
Pasipatan fisik: 2205 stainless steel coiled tube komposisi kimiawi
| Kapadetan (Kg/m3) | 7810 |
| Perméabilitas Magnét (20°C) | <50 |
| Modulus ngora (kN/mm2) | 190 |
| Résistansi Listrik Spésifik, 20°C (µΩ.m) | 0.85 |
| Rata-rata koefisien ékspansi termal, 20-300°C (m/m/oC) | 11 x 10-6 |
| Panas spésifik, 20°C (J/kg.K) | 400 |
| Konduktivitas termal, 20°C (W/mK) |
waktos pos: May-25-2023