Kelas 310/310S stainless steel 8.0*0.3mm coiled tubing/capillary tubing
Komposisi Kimia Kelas 310/310S Stainless Steel
Komposisi kimia kelas 310 sareng kelas 310S stainless steel diringkeskeun dina tabel di handap ieu.
Kelas 310/310S stainless steel 8.0*0.3mm coiled tubing/capillary tubing
Tabél 1.Komposisi kimia% tina kelas 310 sareng 310S stainless steel
| Komposisi Kimia | 310 | 310S |
| Karbon | 0,25 max | 0,08 max |
| Mangan | 2.00 max | 2.00 max |
| Silikon | 1,50 max | 1,50 max |
| Fosfor | 0,045 max | 0,045 max |
| Walirang | 0,030 max | 0,030 max |
| Kromium | 24.00 - 26.00 | 24.00 - 26.00 |
| Nikel | 19.00 - 22.00 | 19.00 - 22.00 |
Sipat mékanis Kelas 310/310S Stainless Steel
Sipat mékanis kelas 310 jeung kelas 310S stainless steel diringkeskeun dina tabel di handap ieu.
Kelas 310/310S stainless steel 8.0*0.3mm coiled tubing/capillary tubing
Tabél 2.Sipat mékanis tina stainless steel kelas 310/310S
| Sipat mékanis | 310/310S |
| Kelas 0,2 % Buktina Stress MPa (min) | 205 |
| Kakuatan Tensile MPa (min) | 520 |
| Elongation% (mnt) | 40 |
| Teu karasa (HV) (max) | 225 |
Pasipatan fisik tina steel steel Ferritic
Sipat fisik kelas 310 jeung kelas 310S stainless steel diringkeskeun dina tabel di handap ieu.
Kelas 310/310S stainless steel 8.0*0.3mm coiled tubing/capillary tubing
Tabél 3.Sipat fisik tina stainless steel kelas 310/310S
| Pasipatan | at | Nilai | Unit |
| Kapadetan |
| 8.000 | Kg/m3 |
| Konduktivitas listrik | 25°C | 1.25 | %IACS |
| Résistansi listrik | 25°C | 0.78 | Mikro ohm.m |
| Modulus élastisitas | 20°C | 200 | GPa |
| Modulus geser | 20°C | 77 | GPa |
| Rasio Poisson urang | 20°C | 0.30 |
|
| Lebur Rnage |
| 1400-1450 | °C |
| Panas spésifik |
| 500 | J/kg.°C |
| Perméabilitas magnét rélatif |
| 1.02 |
|
| Konduktivitas termal | 100°C | 14.2 | W/m.°C |
| Koéfisién ékspansi | 0-100°C | 15.9 | /°C |
| 0-315°C | 16.2 | /°C | |
| 0-540°C | 17.0 | /°C |