Steels steels mangrupakeun steels alloy tinggi nu boga résistansi korosi luhur batan steels séjén alatan ayana jumlah badag kromium dina rentang 4 nepi ka 30%.Baja tahan karat digolongkeun kana martensit, feritik sareng austenitik dumasar kana struktur kristalna.Sajaba ti éta, maranéhna ngabentuk grup sejen katelah steels présipitasi-hardened, nu mangrupakeun kombinasi antara steels martensitic na austenitic.
347H stainless steel coiled tubing
Lembar data di handap ieu bakal masihan langkung rinci ngeunaan baja tahan karat kelas 347H, anu rada hese tibatan baja kelas 304.
347H stainless steel coiled tubing
Tabel di handap nembongkeun komposisi kimia kelas 347H stainless steel.
347H stainless steel coiled tubing
| unsur | Eusi (%) |
|---|---|
| Beusi, Fe | 62.83 – 73.64 |
| Kromium, Cr | 17 – 20 |
| Nikel, Ni | 9 – 13 |
| Mangan, Mn | 2 |
| Silikon, Si | 1 |
| Niobium, Nb (Columbium, Cb) | 0.320 – 1 |
| Karbon, C | 0.04 – 0.10 |
| Fosfor, P | 0,040 |
| Sulfur, S | 0.030 |
Pasipatan fisik
347H stainless steel coiled tubing
Sipat fisik kelas 347H stainless steel dirumuskeun dina tabel di handap ieu.
| Pasipatan | métrik | Kaisar |
|---|---|---|
| Kapadetan | 7,7 – 8,03 g/cm3 | 0,278 – 0,290 lb/in³ |
347H stainless steel coiled tubing
Sipat mékanis
Sipat mékanis kelas 347H stainless steel dipintonkeun dina tabel di handap ieu.
| Pasipatan | métrik | Kaisar |
|---|---|---|
| Kakuatan tensile, pamungkas | 480 MPa | 69600 psi |
| Kakuatan tensile, ngahasilkeun | 205 MPa | 29700 psi |
| Kakuatan beubeulahan (@750°C/1380°F, waktos 100.000 jam) | 38 – 39 MPa, | 5510 - 5660 psi |
| Modulus elastis | 190 – 210 GPa | 27557 – 30458 ksi |
| Babandingan Poisson | 0.27 – 0.30 | 0.27 – 0.30 |
| Elongation dina putus | 29% | 29% |
| Teu karasa, Brinell | 187 | 187 |
Sebutan séjén anu sarua jeung kelas 347H stainless steel kaasup handap:
- ASTM A182
- ASTM A213
- ASTM A240
- ASTM A249
- ASTM A271
- ASTM A312
- ASTM A336
- ASTM A376
- ASTM A403
- ASTM A430
- ASTM A479
- ASTM A813
- ASTM A814
- SAE 30347H