321 stainless steel 8 * 0.75mm coiled tubing
| Australia | AS 2837-1986-321 |
| Jérman | W.Nr 1.4541 X6CrNiTi18 10 |
| Britania Ageung | BS970 Bagian 3 1991 321S31 BS970 - 1955 EN58B / EN58C |
| Jepang | JIS G4303 SuS 321 |
| AS | ASTM A276-98b 321 SAE 30321 AISI 321 UNS S32100 |
321 stainless steel 8 * 0.75mm coiled tubing
| Komposisi Kimia | |||||||||||
| Min.% | Max % | ||||||||||
| Karbon | 0 | 0.08 | |||||||||
| Silikon | 0 | 1.00 | |||||||||
| Mangan | 0 | 2.00 | |||||||||
| Nikel | 9.00 | 12.00 | |||||||||
| Kromium | 17.00 | 19.00 | |||||||||
| titanium | 5 x Karbon | 0.80 | |||||||||
| Fosfor | 0 | 0.045 | |||||||||
| Walirang | 0 | 0.03 | |||||||||
| Sarat Harta Mékanis - Dipasang kana ASTM A276-98b 321 | |||||||||||
| Bérés | Panas bérés | Bérés tiis | |||||||||
| Diaméter atawa ketebalan mm | Sadayana | Nepi ka 12.7 | Leuwih 12.7 | ||||||||
| Kakuatan Temsil Mpa Min. | 515 | 620 | 515 | ||||||||
| Ngahasilkeun Kakuatan Mpa Min. | 205 | 310 | 205 | ||||||||
| Elongation dina 50mm% Min. | 40 | 30 | 30 | ||||||||
| Pasipatan mékanis has dina Suhu Kamar - Annealed | |||||||||||
| Bérés | Digambar Tiis | Lain | |||||||||
| Kakuatan Tensile Mpa | 680 | 600 | |||||||||
| Kakuatan ngahasilkeun Mpa | 500 | 280 | |||||||||
| Elongation dina 50mm% | 40 | 55 | |||||||||
| Dampak Charpy VJ | 180 | ||||||||||
| Teu karasa | HB | 200 | 165 | ||||||||
| Rc | 15 | ||||||||||
| Pasipatan Suhu elevated | |||||||||||
| 321 mintonkeun résistansi oksidasi alus dina layanan kontinyu nepi ka 930oC, sarta dina layanan intermittent nepi ka 870oC. Éta ogé tiasa dianggo dina kisaran présipitasi karbida 430oC – 870oC tanpa résiko korosi intergranular.Sipat mékanis diréduksi nalika suhu naék.321 stainless steel 8 * 0.75mm coiled tubing
| |||||||||||
| Pasipatan mékanis has - Annealed dina Suhu luhur | |||||||||||
| SuhuoC | 20 | 430 | 550 | 650 | 760 | 870 | |||||
| Short - Tés Tensile Time | Kakuatan Tensile Mpa | 580 | 425 | 365 | 310 | 205 | 140 | ||||
| Kakuatan ngahasilkeun Mpa | 240 | 170 | 150 | 135 | 105 | 70 | |||||
| Elongation dina 50mm% | 60 | 38 | 35 | 32 | 33 | 40 | |||||
| Tés ngarayap | Stress pikeun 1% ngarayap dina 10.000 Jam Mpa | 115 | 50 | 14 | |||||||
| Sipat Suhu Low | |||||||||||
| 321 boga sipat suhu low alus teuing jeung ngaronjat tensile jeung kakuatan ngahasilkeun kalawan saeutik leungitna kateguhan dina kaayaan annealed. | |||||||||||
| Pasipatan mékanis has - Annealed dina Suhu Nol jeung Sub-Enol | |||||||||||
| SuhuoC | 0 | -70 | -130 | -180 | -240 | ||||||
| Kakuatan Tensile Mpa | 740 | 900 | 1135 | 1350 | 1600 | ||||||
| Kakuatan ngahasilkeun Mpa | 300 | 340 | 370 | 400 | 450 | ||||||
| Elongation dina 50mm% | 57 | 55 | 50 | 45 | 35 | ||||||
| Pangaruh Charpy J | 190 | 190 | 186 | 186 | 150 | ||||||