2205 stainless steel 4 * 1mm capillary coiled tubing
2205 Duplex Stainless Steel coiled pipah kapiler
Pasipatan mékanis tina Duplex Steel Steel Kelas 2205
2205 stainless steel 4 * 1mm capillary coiled tubing
| Kelas | Tensile Str (MPa) mnt | Kakuatan ngahasilkeun 0,2% Buktina (MPa) mnt | Elongation (% dina 50mm) mnt | Teu karasa-Rockwell C (HR C) | Teuas-Brinell (HB) |
|---|---|---|---|---|---|
| 2205 | 621 | 448 | 25 | 31 max | 293 max |
Pasipatan fisik tina Duplex Stainless Steel 2205
2205 stainless steel 4 * 1mm capillary coiled tubing
| Kapadetan (Kg.m-1) | 7810 |
|---|---|
| Perméabilitas magnét | <50 |
| Modulus ngora (N/mm2) | 190*10^3 |
| Panas spésifik, 20°℃(J.Kg-1.°K-1) | 400 |
| Résistansi Listrik Spésifik, 20 ℃ (uO.m) | 0.85 |
| konduktivitas termal, 20 ℃ | 15 |
| Rata-rata koefisien ékspansi termal | 11*10^6 |
2205 Duplex Stainless Steel Komposisi Kimia:
2205 stainless steel 4 * 1mm capillary coiled tubing
| Sasmita | C | Mn | Si | P | S | Cr | Mo | Ni | N |
|---|---|---|---|---|---|---|---|---|---|
| 2205 (S31803) | ≤0.03 | ≤2.0 | ≤1.0 | ≤0.03 | ≤0.02 | 21.0≤Cr≤23.0 | 2.5≤Mo≤3.5 | 4.5≤Ni≤6.5 | 0.08≤N≤0.20 |
| 2205 (S32205) | ≤0.03 | ≤2.0 | ≤1.0 | ≤0.03 | ≤0.02 | 21.0≤Cr≤23.0 | 3.0≤Mo≤3.5 | 4.5≤Ni≤6.5 | 0.14≤N≤0.20 |
2205 stainless steel 4 * 1mm capillary coiled tubing
Standar Duplex Ss 2205:
- ASTM / ASME: A240 UNS S32205 / S31803
- EURONORM: 1.4462 X2CrNiMoN 22.5.3
- AFNOR: Z3 CrNi 22.05 AZ
- DIN: W.Nr 1.4462
Aplikasi Duplex Ss 2205
2205 stainless steel 4 * 1mm capillary coiled tubing
Sababaraha aplikasi has duplex stainless steel kelas 2205 dibéréndélkeun di handap:
- Éksplorasi minyak jeung gas
- Parabot ngolah
- Angkutan, neundeun, sareng pangolahan kimiawi
- Klorida tinggi sareng lingkungan laut
- Mesin kertas, bak minuman keras, bubur, digester kertas, jsb.
Keunggulan Duplex Ss 2205
2205 stainless steel 4 * 1mm capillary coiled tubing
Duplex Stainless Steel 2205 Dibandingkeun sareng 316L sareng 317L stainless steel austenitic, 2205 langkung unggul dina résistansi korosi anti-pitting sareng crevice.Cai mibanda lalawanan korosi tinggi.Dibandingkeun sareng austenite, koefisien ékspansi termalna langkung handap, konduktivitas termal langkung luhur.
Duplex Stainless Steel 2205 boga kakuatan compressive dua kali tina stainless steel austenitic, sahingga désainer ngurangan beurat maranéhanana dibandingkeun 316L na 317L.The alloy 2205 utamana cocog pikeun pamakéan dina rentang hawa -50 ° F / + 600 ° F sarta bisa dipaké pikeun hawa handap dina larangan parna (utamana pikeun konstruksi dilas).
Résistansi korosi 2205 Duplex Stainless Steel
2205 stainless steel 4 * 1mm capillary coiled tubing
- Korosi seragam, Résistansi korosi tina stainless steel duplex 2205 langkung unggul tibatan 316L sareng 317L dina kalolobaan lingkungan kusabab kandungan kromium (22%), molybdenum (3%), sareng eusi nitrogén (0,18%).
Anti korosi lokal, Eusi kromium, molybdenum, jeung nitrogén dina duplex stainless steel 2205 ngajadikeun eta kacida tahan ka pitting na crevice korosi dina oksidasi jeung solusi asam. - Anti-stress korosi, The 2205 struktur duplex of stainless steel mantuan pikeun ngaronjatkeun daya tahan kana stress korosi cracking tina stainless steel.Dina suhu nu tangtu, dina kaayaan tegangan, oksigén, jeung klorida, klorida stress korosi lumangsung dina stainless steel austenitic.Kusabab kaayaan ieu henteu gampang dikontrol, panggunaan 304L, 316L, sareng 317L diwatesan dina hal ieu.
- Kacapean anti korosi, Dual-fase baja 2205 kakuatan tinggi na lalawanan korosi kana kakuatan kacapean lalawanan korosi tinggi.Alat-alat pangolahan rentan ka lingkungan korosif sareng siklus loading, sareng fitur duplex stainless steel 2205 cocog pikeun aplikasi sapertos kitu.
Metalografi ngeunaan Duplex Ss 2205 uns s31803
Komposisi kimia tina baja duplex 2205 masihan struktur mikro anu dipikahoyong 50 ϫ / 50 saatos 1900 / 1922 ° F (1040 ° C / 1080 ° C) annealing solusi padet.Lamun suhu perlakuan panas leuwih luhur ti 2000 ° F, bisa ngakibatkeun kanaékan komposisi ferrite.Kawas stainless steels duplex sejen, 2205 alloy rentan ka présipitasi fase intermetallic.
Fase intermetallic precipitates antara 1300 ° F jeung 1800 ° F sarta precipitates panggancangna dina 1600 ° F. Ku alatan éta, urang kudu nguji 2205, pikeun mastikeun yén euweuh fase intermetallic, rujukan test ASTM A 923.